性能测试

磁铁性能参数

等级GRADE	剩磁（Br）		磁感矫顽力（Hcb）		内禀矫顽力（Hcj）		最大磁能积(BH)max		工作温度（Tw）℃
等级GRADE	T	KGs	KA/m	KOe	KA/m	KOe	KJ/m³	MG Oe	工作温度（Tw）℃
N35	1.18-1.23	11.8-12.3	≥868	≥10.9	≥955	≥12	263-287	33-36	≤80
N38	1.22-1.28	12.2-12.8	≥899	≥11.3	≥955	≥12	287-310	36-39	≤80
N40	1.26-1.31	12.6-13.1	≥923	≥11.6	≥955	≥12	302-326	38-41	≤80
N42	1.28-1.34	12.8-13.8	≥923	≥11.6	≥955	≥12	318-342	40-43	≤80
N45	1.32-1.37	13.2-13.7	≥876	≥11.0	≥955	≥12	342-366	43-46	≤80
N48	1.36-1.42	13.6-14.2	≥836	≥10.6	≥876	≥11	358-390	45-48	≤80
N50	1.39-1.45	13.9-14.5	≥836	≥10.5	≥876	≥11	374-406	47-51	≤80
N52	1.42-1.48	14.2-14.8	≥796	≥10.6	≥876	≥11	390-422	49-53	≤80
N35M	1.18-1.23	11.8-12.3	≥868	≥10.9	≥1114	≥14	263-287	33-36	≤100
N38M	1.22-1.28	12.2-12.8	≥899	≥11.3	≥1114	≥14	287-310	36-39	≤100
N40M	1.26-1.31	12.6-13.1	≥923	≥11.6	≥1114	≥14	302-326	38-41	≤100
N42M	1.28-1.34	12.8-13.4	≥924	≥11.6	≥1114	≥14	318-342	40-43	≤100
N45M	1.34-1.39	13.4-13.9	≥876	≥11.0	≥1114	≥14	342-366	43-36	≤100
N48M	1.36-1.42	13.6-14.2	≥876	≥11.0	≥1114	≥14	366-390	46-49	≤100
N35H	1.18-1.23	11.8-12.3	≥868	≥10.9	≥1353	≥17	263-287	33-36	≤120
N38H	1.22-1.28	12.2-12.8	≥899	≥11.3	≥1353	≥17	287-310	36-39	≤120
N40H	1.26-1.31	12.6-13.1	≥923	≥11.6	≥1353	≥17	302-326	38-41	≤120
N42H	1.28-1.34	12.8-13.4	≥924	≥11.6	≥1353	≥17	318-342	40-43	≤120
N45H	1.33-1.39	13.3-13.9	≥923	≥11.6	≥1353	≥17	342-366	43-46	≤120
N48H	1.36-1.42	13.6-14.2	≥923	≥11.6	≥1274	≥16	≥366-390	46-49	≤120
N33SH	1.41-1.19	11.4-11.9	≥836	≥10.5	≥1592	≥20	247-270	31-34	≤150
N35SH	1.18-1.23	11.8-12.3	≥868	≥10.9	≥1592	≥20	263-287	33-36	≤150
N38SH	1.22-1.28	12.2-12.8	≥899	≥11.3	≥1592	≥20	287-310	36-39	≤150
N40SH	1.26-1.31	12.6-13.1	≥923	≥11.6	≥1592	≥20	303-326	38-41	≤150
N42SH	1.28-1.34	12.8-13.4	≥923	≥11.6	≥1592	≥20	318-342	40-43	≤150
N45SH	1.33-1.39	13.3-13.9	≥923	≥11.6	≥1592	≥20	342-366	43-46	≤150
N28UH	1.03-1.09	10.3-10.9	≥780	≥9.80	≥1990	≥25	207-231	26-29	≤180
N30UH	1.09-1.14	10.9-11.4	≥812	≥10.2	≥1990	≥25	223-247	28-31	≤180
N33UH	1.13-1.17	11.3-11.7	≥852	≥10.7	≥1990	≥25	247-263	31-33	≤180
N35UH	1.18-1.22	11.8-12.2	≥868	≥10.9	≥1990	≥25	263-287	33-36	≤180
N38UH	1.22-1.27	12.2-12.7	≥899	≥11.3	≥1990	≥25	≥287-310	36-39	≤180
N28EU	1.03-1.09	10.3-10.9	≥780	≥9.80	≥2388	≥30	≥207-231	26-29	≤200
N30EH	1.08-1.13	10.8-11.3	≥812	≥10.2	≥2388	≥30	223-247	28-31	≤200
N33EH	1.13-1.17	11.3-11.7	≥852	≥10.7	≥2388	≥30	247-263	31-33	≤200

Temp. Coeff. of Br(可逆温度系数)	-0.09～-0.11%℃	Temp. Coeff. of Hc(可逆温度系数)	-0.50～-0.60%℃
Density(密度)	7.4～7.6g/cm3	Electrical Resistivity(电阻率)	114 uΩ.cm
Vickers Hardness(韦氏硬度)	600 Hv	Flexural Strength(抗弯强度)	25 Kg/mm
Tesile Strength(抗拉强度)	8.0 Kg/mm3	Coeff. of Thermal Expandion(热膨胀系数)	4×10-6/℃
Specific Heat(比热)	0.12 Kca/（kg, ℃）	Thermal Conductivity(导热系数)	7.7 Kca/(m.h. ℃)
Young’s Modulus(杨氏抗拉强度)	1.6×1011 N/m3	Rigidity(钢性)	0.64 N/m2
Poisson’s Ratio(泊松比)	0.24	Compressibility(压缩率)	9.8×10-12m2/N
Curie Temperature(居里温度)	310-340℃	Relative Recoil Permeability urev(相对磁导率)	1.05